Macro-mesoporous γ-alumina support(MMA) was prepared by a sol-gel route in aqueous medium using pseudo-boehmite as aluminum source and polystyrene microspheres and Pluronic P123 as hard and soft dual templates,respectively.MMA had a BET specific surface area of about 259 m2 g-1,total pore volume of about 1.61 cm3 g-1,macropore diameter of about 102 nm,and mesopore diameter of about 14 nm.Re2O7/MMA and conventional Re2O7/Al2O3 were prepared by a incipient-wetness impregnation method,and their catalytic performances in the metathesis of 1-butene and 2-butene were tested in a fixed-bed tubular reactor.The result showed that Re2O7/MMA possessed higher activity and far longer working life-span than conventional Re2O7/Al2O3.
Lei SangSheng-Li ChenGuimei YuanMin ZhengJu YouAicheng ChenRui LiLanjing Chen
An nc-TiO/SnO inverse opal composite membrane was fabricated,the photoactivity of which was significantly enha...
Sheng-Li Chen~*,Ai-Jun Wang,Chun-Tian Hu,Chao Dai State Key Laboratory of Heavy Oil Processing,College of Chemical Engineering,China University of Petroleum,Changping,Beijing,102249,China
Mesoporous γ-aluminas with large pore size(up to 19 nm,denoted as MA19) are prepared from dispersed pseudo-boehmite using pluronic P123 as template.It is found that these mesoporous alumina supported rhenium oxide catalysts were more active and have far longer working life-span in gas-phase metathesis of 1-butene and 2-butene to propene than rhenium oxide on conventional alumina with small pore size(5 nm).At 60°C and atmospheric pressure with WHSV = 1 h-1,the similar stable conversions of butene(ca.55%) for all the 13 wt% Re 2 O 7 /alumina catalysts were obtained near the chemical equilibrium,and the stable working life-spans of Re 2 O 7 /MA19 were far longer than that of Re 2 O 7 /Al 2 O 3,being about 70 h and 20 h,respectively.
Lei SangSheng-Li ChenGuimei YuanZheng ZhouRui LiAicheng ChenMin ZhengJu You