Precise control of the pore sizes for porous carbon materials is of importance to study the confinement effect of metal particles because the pore size in nanosize range will decide the physical and chemical properties of the metal nanoparticles. In this paper, we report a new approach for the synthesis of iron doped ordered mesoporous carbon materials with adjustable pore size using Fe-SBA-15 as hard template and boric acid as the pore expanding reagent. The pore size can be precisely adjusted by a step of 0.4 nm in the range of 3-6 nm. The carbonization temperature can be lowered to 773 K due to the catalytic role of the doped iron. The present approach is suitable for facile synthesis of metal imbedded porous carbon materials with tunable pore sizes.
Haodong TangGuojun LanJian ZhongHuazhang LiuYing Li
A series of high surface area graphitic carbon materials （HSGCs） were prepared by ball-milling method. Effect of the graphitic degree of HSGCs on the catalytic performance of Ba-Ru-K/HSGC-x （x is the ball-milling time in hour） catalysts was studied using ammonia synthesis as a probe reaction. The graphitic degree and pore structure of HSGC-x supports could be successfully tuned via the variation of ball-milling time. Ru nanoparticles of different Ba-Ru-K/HSGC-x catalysts are homogeneously distributed on the supports with the particle sizes ranging from 1.6 to 2.0 nm. The graphitic degree of the support is closely related to its facile electron transfer capability and so plays an important role in improving the intrinsic catalytic performance of Ba-Ru-K/HSGC-x catalyst.
Wei JiangYing LiWenfeng HanYaping ZhouHaodong TangHuazhang Liu