A large amount of one-dimensional ZnO nanorods with diameters in 15―50 nm aligned in radial cluster were successfully synthesized by polar polymer polyvinyl alcohol (PVA) as soft-template. The growth of ZnO nanorods was controlled by changing annealing temperature. The evolution of the morphology and microstructure was investigated by scanning electron microscope, transmission electron micro- scope and X-ray diffraction. It is shown that ZnO nanorods tend to be uniform and the crystallization is gradually improved with the temperature increasing from 400℃ to 700℃. The photoluminescence spectra of products show a strong ultra violet emission and relatively weak defect emissions. The sharp strong emission peak at 354 nm owing to the inter-band transition indicates the extraordinary photoluminescence property of ZnO nanorods.
LI JiangYongLI LanXU JianPingZHANG XiaoSongLI HaiYanZHUANG JinYan
High-efficient Tb^3＋ activated SrAl2O4 phosphor was synthesized by a combined combustion-solid-state reaction method. The precursor of SrAl2O4：Th^3＋ phosphor was prepared via a combustion process, and then the as-prepared powder was heated in a reductive ambient of activated carbon at 1250 ℃ for 1 h. The results of X-ray diffraction, scanning electron microscopy, and photoluminescence spectra revealed the influence of the dosage of urea and heated process on the crystallinity, morphology, and photoluminescence of the phosphor. Comparing with traditional solid-sate reaction, the crystallinity and emission intensity of the SrAl2O4：Tb^3＋ phosphor were improved by this two-step process.