The directional structure of Ni60/high-aluminum bronze composite coating was formed using induction remelting and forced cooling.The microstructural evolution and the characteristics of interface growth were studied.The results showed that the remelted coating formed metallurgical bonding with the substrate.The micros tructures changed from plane crystal to dendrite,cellular dendrite,fine cellular dendrite,and then to dendrite again with the increase in the cooling rate.The crystal grew along the heat flow direction and had(111) and(200)preferred orientations when the cooling rate was 1.886 ml-min^(-1).mm^(-2).The plane crystal,dendrite and cellular dendrite were mainly composed of compounds and solid solutions with Ni,Fe and Cu,and they were surrounded by strengthening phases composed of Cr,C and B.The grain boundary of directional structure coatings showed the characteristic of regular eutectic growth,but grain boundary of remelted coating presented characteristic of divorced eutectic growth.The wear resistance of directional structure coatings is better than that of remelted coating.
Xiao-Tian YangXiu-Qian LiQiang-Bin YangJun-Ling DuanXiao-Yue FuHeng-Li WeiWen-Sheng Li
The Ni60/15wt% Cu directional structure coating was prepared by the composite technology of flame spraying, induction remelting,and forced cooling, and the effect of Cu on the microstructure, phase, hardness, and wear performance of Ni60 coatings was investigated. Results showed that Cu addition makes the microstructure of Ni60 directional structure coating more compact, and Cu is mainly enriched within the crystal grain, resulting in the formation of Cu_(3.8)Ni as the bonding phase. Compared with Ni60 directional structure coating, Ni60/Cu directional structure coating has a lower hardness, lower friction coefficient, and lower wear rate, which indicate that Cu can effectively enhance the antifriction performance of Ni60 directional structure coating.
Xiaotian YangXinhua WangJun ZhouHengli WeiRong ZengWensheng Li