Pyrolysis has the potential of transforming waste into recyclable products. Pyrolytic carbon black (PCB) is one of the most important products from the pyrolysis of used tires. Techniques for surface modifications of PCB have been developed. One of the most significant applications for modified PCB is to reinforce the rubber matrix to obtain high added values. The transverse relaxation and the chain dynamics of vulcanized rubber networks with PCB and modified PCB were studied and compared with those of the commercial carbon blacks using selective 1H transverse relaxation (T2) experiments and dipolar correlation effect (DCE) experiments on the stimulated echo. Demineralization and coupling agent modification not only intensified the interactions between the modified PCB and the neighboring polyisoprene chains, but also increased the chemical cross-link density of the vulcanized rubber with modified PCB. The mechanical testing of the rubbers with different kinds of carbon blacks showed that the maximum strain of the rubber with modified PCB was improved greatly. The mechanical testing results confirmed the conclusion obtained by nuclear magnetic resonance (NMR). PCB modified by the demineralization and NDZ-105 titanate coupling agent could be used to replace the commercial semi-reinforcing carbon black.
Pyrolysis has the potential of transforming waste into valuable products. Pyrolytic carbon black (PCB) is one of the most important products resulting from the pyrolysis of used tires. One of the most significant applica-tions of modified pyrolytic carbon black is its use as pigment for offset printing ink to obtain high added values. Inverse gas chromatography (IGC) results show that a large quantity of inorganic matters and carbonaceous deposit are removed by treating the pyrolytic carbon black with nitric acid solution. Plenty of active sites originally occu-pied by inorganic ash and coke are recovered. The surface energy of pyrolytic carbon black (TWPC)modified by titanate-coupling agent-especially the specific interaction γ sspdetermined by the specific probe molecule, tolu-ene-shows the strong interaction between the TWPC and the synthetic resins. The offset printing ink performance confirms the IGC prediction. And TWPC has the great potential of applications in printing ink industry as pigment.