Cobalt-doped Bi2Se3 topological insulators have been grown though melt-grown reaction. The Bi2Se3 matrix is diamagnetic and doped sample is a superposition of ferromagnetism （FM） and paramagnetism （PM） behavior at low tem- perature. The values of Msmol, Hc, and Mr increase as the Co concentration increases. Two possible explanations have been proposed for the origin of ferromagnetism in Co-doped Bi2Se3. One is the magnetic ordering from nanoclusters of Co-Se compound in the crystals, and the other is Ruderman-Kittel-Kasuya-Yosida （RKKY） interaction between magnetic impurities.
Perovskite-based materials can be widely used in the aerospace and transportation field. Perovskite man-ganese oxides La0.7Sr0.3MnO3 （LSMO） thin films were grown on LaAlO3 （100） and Si （100） single crystal sub-strates by the polymer-assisted chemical solution deposi-tion （PACSD） method. Electronic transport behavior, microstructure, and magnetoresistance （MR） of LSMO thin films on different substrates were investigated. The resis-tance of LSMO films fabricated on LaAlO3 substrates is smaller than that on the Si substrates. The magnetic field reduces resistance of LSMO films both on Si and LAO in the wide temperature region, when the insulator-metal transition temperature shifts to higher temperature. The low-field magnetoresistance of LSMO films on Si in low temperature range at 1 T is larger than that of LSMO films on LAO. However, the MR of LSMO film on LAO films at room-temperature is about 5.17%. The thin films are smooth and dense with uniform nanocrystal size grain. These results demonstrate that PACSD is an effective technique for producing high quality LSMO films, which is significant to improve the magnetic properties and the application of automotive sensor.