A series of samples of hexagonal boron nitride-aluminum nitride ceramic composites with different amounts of CaF2 as sintering aid were prepared by spark plasma sintered at 1700-1850 ℃ for 5 min.The addition of CaF2 effectively lowered the sintering temperature and promoted the densification of AlN-BN composites.With the increase of sintering temperature,the density increased,and the contiguity of AlN grains enhanced in AlN-BN composites.Thermal conductivity of AlN-BN composites increased with the increase in CaF2 content and sintering temperature,and there is a maximum value of 78.6 W·m^-1·K^-1 when the sample with 3wt% CaF2 sintered at 1800 ℃.
The environment-friendly glasses which integrate function and structure were introduced, among these glasses can save energy very efficiently due to its low infrared emissivity. The fundamental principle of the low emissivity glass and the research progress of this kind glass were analyzed. Meanwhile, high performance and low applied development trend of emissivity glass were reviewed.