Oxide films formed on the surfaces of Fe-based bulk metallic glasses in the temperature range between 373 K and 573 K were characterized and their effects on the corrosion behaviors were investigated by microstructural and electrochemical analysis. The oxide film formed at 573 K is iron-rich oxide and it exhibits an n-type semiconductor at a higher potential than 0.35 V and a p-type semiconductor at a lower potential than 0.35 V. Capacitance measurements show that the donor density decreases with the increase in oxidation temperature, while the thickness of the space charge layer increases with the oxidation temperature rising. The result of immersion tests shows that the mass loss rate increases with the oxidation temperature rising. Therefore, the correlation between microstructure and corrosion resistance needs to be proposed because the corrosion resistance is deteriorated with the development of the oxide films.
Hong-xiang LiShan-lin WangYeonuk JeongSeonghoon Yi
Aer Met100 ultra-high strength steel plates with a thickness of 2 mm were welded using a CO2 laser welding system. The influences of the welding process parameters on the morphology and microstructure of the welding joints were investigated, and the mechanical property of the welding joints was analyzed. The experimental results showed that the fusion zone of welding joint mainly consisted of columnar grains and a fine dendrite substructure grew epitaxially from the matrix. With the other conditions remaining unchanged, a finer weld microstructure was along with the scanning speed increase. The solidification microstructure gradually transformed from cellular crystal into dendrite crystal and the spaces of dendrite secondary arms rose from the fusion line to the center of the fusion zone. In the fusion zone of the weld, the rapid cooling caused the formation of martensite, which led the microhardness of the fusion zone higher than that of the matrix and the heat affected zone. The tensile strength of the welding joints was tested as 1 700 MPa, which was about 87% of the matrix. However, the tensile strength of the welding joints without defects existed was tested as 1832 MPa, which was about 94% of the matrix.