Magnetic nano zinc ferrite fliuds were synthesized using an improved liquid phase chemical method, which would be used to replace tradditional iron oxides magnetic material. A novel copolymer （PLAA） with D, L-lactide （D, L-LA） and alanine was synthesized using stannous octoate as initiator. Magnetic polymer microspheres were fabricated with nano zinc ferrite fluid coated with alanine modified poly lactide. These as-prepared zinc ferrite fluids, modified poly lactide and magnetic composites, were characterized with X-ray diffraction diffractometer, FT-IR spectrometer, nuclear magnetic resonance spectrometer, scanning electron microscope, transmission electron microscope, vibrating sample magnetometer, and thermogravimetric analyzer. The results demonstrate that the as-prepared zinc ferrite is spinel type of ZnFe2O4 nano crystals with particle size of 20-45 nm and magnetization of 32×10^-3 A.m2. Alanine is copolymerized with lactide, and the prepared composite magnetic microsphere is coated with the modified polylactide, with mass fraction of 45.5% of PLA, particle size ranging from 80-300 nm, and magnetization of 10.6×10^-3 A·m^2, which suggests ZnFe2O4 enjoys a stable magnetization after being coated by polymer.
D,L-lactide was prepared from D,L-lactic acid by means of polymerization and depolymerization at low vacuum level.Morpholine-2,5-dione(MD) was synthesized from the cyclization of chloroacetyl glycine which was made from chloroacetyl chloride and glycine in the basic condition.A novel copolymer(PLAMD) with D,L-lactide(D,L-LA) and morpholine-2,5-dione(MD) was synthesized using stannous octoate as initiator,and characterized with FT-IR and 1HNMR.The biocompatibility of PLAMD and PLA was investigated by MTT and microscope.The results show that amino acid is introduced into PDLLA main chain.PLAMD has better cell affinity than PLA,so it is a promising biomaterial.