A novel magnetic anion exchange resin NDM-1 was prepared through suspension polymerization and then functionalized with ammonolysis and alkylating agents.Its application for selective removal of nitrate was performed in comparison with MIEX.The results demonstrated that NDM-1 achieved higher efficiency in nitrate removal than MIEX did,with or without the existence of competing anion SO_4^2- ascribed to its longer alkyl chains on exchange sites.Combined with the advantage of easy separation due toγ-Fe_2O_3 implanted,the magnetic anion exchange resin NDM-1 was considered to be superior to MIEX for nitrate removal in practical application.
Yang ZhouChen Dong ShuangQing ZhouMan Cheng ZhangPeng Hui LiAi Min Li
Bilayer-silane-coated Fe304 nanoparticles with inner layer of tetraethoxy silane （TEOS） and outer layer of vinyltriethoxysilane （VTEO） were generated to enhance their acid resistance. These nanoparticles were copolymerized with vinylbenzyl chloride （VBC） using suspension polymerization, and then post-crosslinked. The resulting hypercrosslinked magnetic resin M150 presented specific bimodal property with large specific surface area of 1109 m2/g. It exhibited more excellent adsorption capacity of p- nitrophenol compared to another two magnetic adsorbents Q150 and MIEX~. Moreover, the acid stable property of the magnetite in MI50 extended its application at low pH value.