Adopting LB film method, an arachidic acid （AA）/PEDOT multilayer LB film was chosen, and polymerized EDOT monomers in hydrophilic group of LB to prepare arachidic acid （AA）/PEDOT multilayer LB film. UV-Vis, FT-IR and XPS analyses implied that EDOT was effectively polymerized in film, and thus PEDOT conducting polymer was produced. Analyses of XRR and SIMS indicated that film had a well-arranged lamella structure, and further research showed that polymerization of EDOT in AA film destroyed the orderliness of the original LB film. This phenomenon could be related to the destructive effect of polymerization on layered structure. We used four-point probe and semiconductor instrument to study the conductivity property of the film, and observed that the conductivity of AA/PEDOT film had sudden changes with the processing time of changes in effective conduction network. That was caused by ＂permeability＂ in conducting channel of multilayer film. The test results also indicated that the conductivity of AA/PEDOT film was obviously better than that of spin-coating PEDOT/PSS film or that of ODA-SA/PEDOT-PSS film, which was due to the higher π structure of PEDOT structure and ordered film structure.