Two new isostructural multi-metal beryllium borates, m^3 Li Na4Be4B10O24F（M = Sr（1）, Cd（2））, have been synthesized by spontaneous crystallization. The structures were verified by single-crystal X-ray crystallography. The compounds crystallize in the trigonal space group R 3, with a = b = 9.4645（1） A, c = 38.842（8） A, V = 3013.2（6） A3, Z = 6, F（000） = 2568, Dc = 3.005 g/cm^3, Mr = 908.9, R = 0.0327, w R = 0.0678, μ = 8.160 mm-1 for Sr3 Li Na4Be4B10O24F and a = b = 9.3019（8） A, c = 37.782（7） A, V = 2831.12（9） A3, Z = 6, F（000） = 2748, Dc = 3.459 g/cm^3, Mr = 983.24, R = 0.0158, w R = 0.0455, μ = 3.586 mm-1 for Cd3 Li Na4Be4B10O24F. The structures are characterized by an infinite two-dimensional [Be8B16O40F2]∞ double layer bridged by [B12O24] groups like a sandwich structure, while the cations reside in tunnels along different directions. UV-vis-IR diffuse reflectance spectroscopy demonstrates that their cut-off edges are below 200 nm. Thermal analysis shows that they melt incongruently and their melting points are around 740-770 ℃.
We develop a picosecond widely tunable laser in a deep-ultraviolet region from 175 nm to 210 nm, generated by two stages of frequency doubling of a 80-MHz mode-locked picosecond Ti：sapphire laser. A β-BaB2O4 walk-off compensation configuration and a KBe2BO3F2 prism-coupled device are adopted for the generation of second harmonic and fourth harmonics, respectively. The highest power is 3.72 mW at 193 nm, and the fluctuation at 2.85 mW in 130 rain is less than ±2%.
We demonstrate a high power high beam quality diode-pumped 1 112-nm Nd：YAG master-oscillator power-amplifier （MOPA） laser system. To increase the extraction efficiency and output power, a four-pass amplifier scheme is employed. Finally, the injected laser output power is amplified from 26 to 64 W with beam quality factor M2=2.85. Furthermore, a theoretical model that takes the temporal overlap inversion number dynamics into account is employed to analyze the performance of the MOPA laser system, and a good agreement with the experimental data is obtained.