β-Sialon/ZrN/ZrON composites were successfully fabricated by an in-situ carbothermal reduction？nitridation process with fly ash, zircon and active carbon as raw materials. The effects of raw materials composition and holding time on synthesis process were investigated, and the formation process of the composites was also discussed. The phase composition and microstructure of the composites were characterized by means of XRD and SEM. It was found that increasing carbon content in a sample and holding time could promote the formation of β-Sialon, ZrN and ZrON. The proper processing parameters to synthesize β-Sialon/ZrN/ZrON composites were mass ratio of zircon to fly ash to active carbon of 49：100：100, synthesis temperature of 1550 °C and holding time of 15 h. The average grain size ofβ-Sialon and ZrN（ZrON） synthesized at 1550 °C for 15 h reached about 2 and 1μm, respectively. The fabrication process ofβ-Sialon/ZrN/ZrON composites included the formation ofβ-Sialon and ZrO2 as well as the conversion of ZrO2 to ZrN and ZrON.
β-Sialon based composites were successfully prepared from fly ash and carbon black under nitrogen atmosphere by carbothermal reduction-nitridation process. Effects of heating temperature and raw materials composition on synthesis process were investigated, and the formation process of the composites was also discussed. The phase composition and microstructure of the composites were characterized by X-ray diffraction and scanning electronic microscopy. The results show that increasing heating temperature or mass ratio of carbon black to fly ash can promote the formation of β-Sialon. The β-Sialon based composites can be synthesized at 1723 K for 6 h while heating the sample with mass ratio of carbon black to fly ash of 0.56. The as-received β-Sialon in the composites exists as granular with an average particle size of 2-3 μm. The preparation process of β-Sialon based composites includes the formation of O′-Sialon, X-Sialon and β-Sialon as well as the conversion processes of O′-Sialon and X-Sialon to β-Sialon.
Spinel compounds LiNi0.5Mn1.3Ti0.2O4（LNMTO） and Li4Ti5O12 （LTO） were synthesized by different methods. The particle sizes of LNMTO and LTO are 0.5-2 and 0.5-0.8 μm, respectively. The LNMTO/LTO cell exhibits better electrochemical properties at both a low current rate of 0.2C and a high current rate of 1C. When the specific capacity was determined based on the mass of the LNMTO cathode, the LNMTO/LTO cell delivered 137 mA.h.g-1 at 0.2C and 118.2 mA-h-g-l at 1C, and the corresponding capacity retentions after 30 cycles are 88.5% and 92.4%, respectively.
Guo-qiang LiuXi WangYa-jie GaoLei WenGuang-yin LiuJian-jie ZhengPeng CenYing Li