The electron beam welding-brazing being used to join 5A06 Al alloy to TC4 Ti alloy decreases the formation of brittle intermetallic compound.Experiments were carried out to study the influence of electron beam welding parameters on the tensile strength of welds,based on an orthogonal test and analysis method.The welding parameters include beam current,welding speed,scanning figure,scanning frequency,figure size,beam offset and focus current.The optimum parameters for3 mm 5A06 Al alloy and 2 mm TC4 alloy were as follows：acceleration voltage was 60 kV,beam current was 11 mA,welding speed was 600 mm/min,focus current was 0 mA,scan figure was O,scanning frequency was 1 000 Hz and beam offset was 0.5 mm.The results show that the joints were with good appearance and quality welded by the optimum parameters.The successful joints could be gained and the maximum tensile strength of Al/Ti dissimilar alloy joints could be up to 222.61 MPa using electron beam welding-brazing.
Cracks may easily occur in the fusion weld between vanadium alloys and stainless steel due to the brittle intermetallics and welding stress. The high vacuum electron beam braze-welding has been successfully used to join vanadium alloy（V-5Cr-STi） to stainless steel （HR-2） with electroplated Cu and Ag coating. To investigate the effects of electroplated coating on the weldability, the joint appearaace, the microstrueture and the mechanical properties of the joints have been thoroughly analyzed. The results show that the joint surface configuration was good and root reinforcement was full and smooth. A reaction zone （RZ） was gained on the interface between the V-5 Cr-5 Ti alloy and HR-2 stainless steel base metals. The width of reaction zone at the top of the joint was up to O. 65 mm, wider than that in the bottom of the joint （ 0.46 mm）. The reaction zone consisted of considerably smaller dendritic structures with an average grain size of less than 10μm. Element Ag and Cu almost enriched the interface between V-SCr-5Ti alloy substrate and RZ, serving as a physical barrier which decreases or avoids the formation of intermetallics. The maximum tensile strength of vanadium alloy^stainless steel dissimilar alloy joint was more than 300 MPa. The joint was defects free.