A series of novel Sm3＋-doped LiY（MoO4）2 red phosphors under the UV excitation were synthesized by solid state reaction at 800 ℃ for 7 h. The data measured by X-ray diffraction （XRD） indicated that the samples were all pure phases of LiY（MoO4）2. Their excitation spectra had a broad band ranging from 250 to 350 nm and several sharp peaks. The centers of the peaks were located at about 365 nm （6H5/2→4D3/2）, 378 nm （6H5/2→rp7/2）, 406 nm （6H5/2→4FT/2）, 420 nm （6H5/2→6ps/2）, 442 nm （6H5/2→4Gg/2）, 471 nm （6H5/2→4I13/2） and 482 nm （6H5/2→419/2）, respectively. The strongest emission was excited by 406 nm, and the main emissions were located at 568 nm （4G5/2→6Hs/2）, 610 nm （4Gs/2→rH7/2）, 649 nm （4G5/2→6H9/2） and 710 nm （4Gs/2→6HII/2）. Photoluminescence prop- erties were determined for various concentrations of Sm3＋-doped LiY（MoO4）2 host, and the luminescence intensity had the best value when x=0.02 in LiYix（MoO4）2：xSm3＋.