TiO2-coated SnO2 （TCS） hollow spheres, which are new anode materials for lithium ion （Li-ion） batteries, were prepared and characterized with X-ray diffraction （XRD）, scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, cyclic voltammetry （CV）, and galvanostatic charge/discharge tests. The results obtained from XRD, SEM, and TEM show that TiO2 can be uniforrrdy coated on the surface of SnO2 hollow spheres with the assistance of anionic surfactant. The cyclic voltammograms indicate that both TiO2 and SnO2 exhibit the activity for Li-ion storage. The charge/discharge tests show that the prepared TCS hollow spheres have a higher reversible coulomb efficiency and a better cycling stability than the uncoated SnO2 hollow spheres.
YI JinLI XiaopingHU ShejunLI WeishanZENG RonghuaFU ZhaoCHEN Lang
With the assistance of nonionic surfactant （OP-10） and surface-selective surfactant （CH3COOH）, anatase TiO2 was prepared as an anode material for lithium ion batteries. The morphology, the crystal structure, and the electrochemical properties of the prepared anatase TiO2 were characterized by scanning electron microscopy （SEM）, X-ray diffraction （XRD）, electrochemical impedance spectroscopy （EIS）, and galvanostatic charge and discharge test. The result shows that the prepared anatase TiO2 has high discharge capacity and good cyclic stability. The maximum discharge capacity is 313 mAh.g^-1, and there is no significant capacity decay from the second cycle.
YI Jin,TAN Chunlin,LI Weishan,LEI Jianfei,and HAO Liansheng School of Chemistry and Environment & Key Laboratory of Electrochemical Technology on Energy Storage and Power Generation of Guangdong Higher Education Institutes,South China Normal University,Guangzhou 510006,China
The authors reported a facile method for the synthesis of manganese dioxide without any template and catalyst at a low-temperature. The prepared sample was characterized with X-ray diffraction（XRD）, scanning electron microscopy（SEM）, Brunauer-Emmett-Teller（BET） surface analysis, Fourier transform infrared（FTIR） spectrometry, cyclic voltammetry, alternative current（AC） impedance test and battery discharge test. It is found that the prepared sample belongs to α-MnO2 and has a microsphere morphology and a large BET surface area. The electrochemical characterization indicates that the prepared sample displays a larger electrochemical capacitance than the commercial electrolytic manganese dioxides（EMD） in Na2SO4 solution, and exhibits larger discharge capacity than EMD, especially at a high rate discharge condition when it is used as cathode of alkaline Zn/MnO2 battery.