The microstructure evolution of the Mg 5Zn 0.63Er（mass fraction,%） alloy containing quasicrystalline phase（I-phase） under the as-cast condition was investigated via different heat treatments.The results show that apart from the precipitation of the W-phase particles,the I-phase almost dissolves into the matrix after solid solution treatment at 480℃ for 10 h（T4 state）.The solution-treated alloy was aged at 175℃ for 6-100 h（T6 state）.The ultimate tensile strength of the peak-aged alloy is approximately 261 MPa companying with an elongation of 10.5%.The improvement of the tensile strength is mainly attributed to the presence of the rod-like MgZn 2 particles.